I-3003 yialloyi ye-AL-Mn, eyi-aluminiyam echasene nomhlwa esetyenziswa ngokubanzi.Amandla ale alloy ayiphezulu kwaye ayinakomelezwa ngonyango lobushushu.Ngoko ke, indlela yokusebenza ebandayo isetyenziselwa ukuphucula iimpawu zayo zomatshini: ineplastiki ephezulu kwi-anneal state., Kwi-semi-cold work hard, i-plasticity iselungile, kwaye ukuqina komsebenzi obandayo kuphantsi kweplastiki, ukuxhathisa okulungileyo kokuhlwa, ukuxhamla okulungileyo, kunye nokungahambi kakuhle.Ikakhulu isetyenziselwa iindawo ezinomthwalo ophantsi ezifuna iplastiki ephezulu kunye ne-weldability efanelekileyo, esebenza kulwelo okanye kwi-gas medium, njengamatanki amafutha, i-petroli okanye i-oyile yokuthambisa i-oyile, izitya ezahlukeneyo zolwelo kunye nezinye iindawo ezincinci zomthwalo ezenziwe ngomzobo onzulu: Ucingo lusetyenziswa. ukwenza iirivets.
Ukumelana nomhlwa kwe-3003 i-alloy ye-aluminium ilungile kakhulu, isondele kwi-corrosion resistance ye-aluminiyam ecocekileyo ye-industrial, kwaye inokumelana ne-corrosion efanelekileyo emoyeni, amanzi ahlambulukileyo, amanzi olwandle, ukutya, i-asidi ye-organic, i-petroli, isisombululo setyuwa engathathi hlangothi, njl njl. Ukumelana nako kuhle kakhulu.
I-3A21 intonga ye-aluminiyam yeyezo zombini i-aluminiyam enzima kunye ne-alloy ekhandiweyo ye-aluminium ngokokwakheka.Xa kuthelekiswa ne-23A21, ngenxa yomxholo ophezulu wobhedu, amandla aphezulu kwaye amandla ashushu angcono, kodwa iplastiki kwindawo eshushu ayilungile njenge-3A21., I-3A21 i-alloy ye-aluminiyam inobuchule obuhle, i-welding efanelekileyo yoqhagamshelwano, i-spot welding kunye ne-rolling welding performance, i-arc welding kunye ne-gas welding ukusebenza kakubi;unyango olushushu lunokomelezwa, kukho umphumo we-extrusion.
I-3003 ye-aluminium intonga yokwakheka kweekhemikhali kunye neempawu zomatshini
Al | Si | Cu | Mg | Zn | Mn | Ti | Ni | Fe+Ni | Fe |
余量 | ≤0.60 | 0.05-0.20 | --- | ≤0.10 | 1.00-1.50 | --- | --- | --- | ≤0.70 |
I-TensileStrength(Mpa) | 140-180 |
yield strength (Mpa) | ≥115 |
EL(%) | ≤2% |
Ubuninzi (g/cm³) | 2.75 |
Ukubunjwa kweekhemikhali kunye neepropati zemishini ye-3A21 intonga ye-aluminium
Al | Si | Cu | Mg | Zn | Mn | Ti | Ni | Ti+Zr | Fe |
umda | ≤0.60 | ≤0.20 | ≤0.50 | ≤0.10 | 1.00-1.60 | ≤0.15 | --- | ≤0.20 | ≤0.70 |
I-TensileStrength(Mpa) | 140-180 |
yield strength (Mpa) | ≥115 |
EL(%) | ≤2% |
Ubuninzi (g/cm³) | 2.75 |